ZRPA12 ( PA12 Nylon Powder )
PHYSICAL CHARACTERISTICS |
Grain Size50~55μm ShapeSpherical Apparent density≥0.40 g/cm³ |
THERMAL PROPERTY |
Melting Point182~185℃(10℃/min) Melting Enthalpy≥90 J/g HDT83.8℃ @1.8MPa / 146.1℃ @0.45MPa |
MOLDING PERFORMANCE |
Density0.97 g/cm³ Tensile Modulus1600 MPa Tensile Strength43 MPa Elongation at break≥15 % Un-notched Impact Strength20.7 KJ/m² Notched Impact Strength3.8 KJ/m² Bending Modulus1432 MPa Bending Strength57 MPa |
GF100 ( Glass Fiber Composite Nylon Powder )
PHYSICAL CHARACTERISTICS |
Apparent density≥0.66 g/cm³ |
THERMAL PROPERTY |
Melting Point183℃（10℃/min） HDT89℃ @1.8MPa / 163℃ @0.45MPa |
MOLDING PERFORMANCE |
Density1.24 g/cm³ Tensile Modulus3498 MPa Tensile Strength43 MPa Elongation at break5 % Un-notched Impact Strength19.26 KJ/m² Notched Impact Strength4.11 KJ/m² Bending Modulus2413 MPa Bending Strength67 MPa |
MF100 ( Mineral Fiber Composite Nylon Powder )
PHYSICAL CHARACTERISTICS |
Apparent density≥0.53 g/cm³ |
THERMAL PROPERTY |
Melting Point180℃（10℃/min） HDT125℃ @1.8MPa / 170℃ @0.45MPa |
MOLDING PERFORMANCE |
Density1.18 g/cm³ Tensile Modulus6128 MPa Tensile Strength50 MPa Elongation at break4.6 % Un-notched Impact Strength20.75 KJ/m² Notched Impact Strength5.58 KJ/m² Bending Modulus4630 MPa Bending Strength74 MPa |
ZRTPU ( Thermoplastic Polyurethanes Powder )
PHYSICAL CHARACTERISTICS |
Grain Size60μm ShapeSpherical Apparent density0.47 g/cm³ |
THERMAL PROPERTY |
Melting Point165℃ HDT |
MOLDING PERFORMANCE |
Density1.15 g/cm³ Tensile Modulus61 MPa Tensile Strength21 MPa Elongation at break310 % Tear strength101 N/mm Bending Modulus74 MPa Bending Strength3.3 MPa |